>Fracture in Phenolic Impregnated Carbon Ablator
【2h】
Fracture in Phenolic Impregnated Carbon Ablator
展开▼
机译:酚醛浸渍碳烧蚀剂的断裂
展开▼
免费
页面导航
摘要
著录项
引文网络
相似文献
相关主题
摘要
The thermal protection materials used for spacecraft heat shields are subjected to various thermal-mechanical loads during an atmospheric entry which can threaten the structural integrity of the system. This paper discusses the development of a novel technique to understand the failure mechanisms inside thermal protection materials. The focus of research is Phenolic Impregnated Carbon Ablator (PICA). It has successfully flown on the Stardust spacecraft and is the TPS material chosen for the Mars Science Laboratory (MSL) and Dragon spacecraft. Although PICA has good thermal properties, structurally, it is a weak material. In order to thoroughly understand failure in PICA, fracture tests were performed on FiberForm* (precursor of PICA), virgin and charred PICA materials. Several samples of these materials were tested to investigate failure mechanisms at a microstructural scale. Stress-strain data were obtained simultaneously to estimate the fracture toughness. It was found that cracks initiated and grew in the FiberForm when a critical stress limit was reached such that the carbon fibers separated from the binder. However, both for virgin and charred PICA, crack initiation and growth occurred in the matrix (phenolic) phase. Both virgin and charred PICA showed greater strength values compared to FiberForm coupons, confirming that the presence of the porous matrix helps in absorbing the fracture energy.
展开▼