Thermally stable composite system Al2O3-Ce 0.75Zr0.25O2 for automotive three-way catalysts

摘要

Present-day three-way catalysts operate in contact with exhaust gases whose temperature is as high as >1000 C, so the problem of developing thermally stable catalytic compositions is still topical. A series of Al2O 3-Ce0.75Zr0.25O2 composites containing 0, 10, 25, and 50 wt % Al2O3 has been synthesized by direct precipitation. The as-prepared composites and those calcined in air at 1000 and 1100 C have been characterized by BET, X-ray diffraction, transmission electron microscopy, and temperature-programmed reduction methods. The composites aged at 1050 C in a 2% O2 + 10% H2O + 88% N2 atmosphere have been used to prepare monolith catalysts, and the oxygen storage capacity (OSC) of the latter has been measured using a gas analysis setup. As the proportion of Al2O 3 in the composite is raised, the mixing uniformity and degree of dispersion of Ce x Zr1-x O2-δ particles increase, their chemical composition becomes homogeneous, and the amount of cerium involved in oxidation and reduction increases. The composite containing 50 wt % Al2O3 is a mixture of Ce x Zr 1-x O2-δ and Al2O3 crystallites, whose size is practically unaffected by calcination. The (Pt/Al2O3 + Al2O3-Ce 0.75Zr0.25O2) based on this composite has the highest OSC and is the most active. For this reason, full-scale testing of this catalyst is recommended. © 2013 Pleiades Publishing, Ltd.