Improvement of composition of CdTe thin films during heat treatment in the presence of CdCl2

摘要

CdCl2 treatment is a crucial step in development of CdS/CdTe solar cells. Although this rocessing step has been used over a period of three decades, full understanding is not yet achieved. This paper reports the experimental evidence for improvement of composition of CdTe layers during CdCl2 treatment. This investigation makes use of four selected analytical techniques; Photo-electro-chemical (PEC) cell, X-ray diffraction (XRD), Raman spectroscopy and Scanning electron microscopy (SEM). CdTe layers used were electroplated using three Cd precursors; CdSO4, Cd(NO3)2 and CdCl2. Results show the improvement of stoichiometry of CdTe layers during CdCl2 treatment through chemical reaction between Cd from CdCl2 and elemental Te that usually precipitate during CdTe growth, due to its naturaludbehaviour. XRD and SEM results show that the low-temperature (~85ºC) electroplated CdTe layers consist of ~(20-60) nm size crystallites, but after CdCl2 treatment, the layers show drastic recrystallisation with grains becoming a few microns in size. These CdCl2 treatedudlayers are then comparable to high temperature grown CdTe layers by the size of grains.