BN nanotubes were successfully grown over iron impregnated MCM-41 at audrelatively low temperature of 750oC for 1 hour by CVD technique.udud BN nanotubes were obtained after the purification procedure including HCl and HNO3 treatments to remove impurities. udud SEM image showed the formation of nano-fibrous network BN structures in the diameter range of 20 nm to 40 nm. udud Both XRD and FTIR characterization results supported the formation of h-BN and c-BN nanostructures.udud Oxidative TGA results indicated that the synthesized BN nanostructures were thermally stable at temperatures higher than 550oC. udud Hydrogen storage measurements via IGA showed that BNNTs could adsorb 0.85 wt% hydrogen which was two times larger than for commercial CNTs. ud
展开▼
机译:通过CVD技术在相对较低的750oC低温下成功地在含铁的MCM-41上生长了BN纳米管1小时。经过HCl和HNO3处理以去除杂质后,纯化得到了BN纳米管。扫描电镜图像显示了直径在20 nm至40 nm范围内的纳米纤维网络BN结构的形成。 XRD和FTIR表征结果均支持h-BN和c-BN纳米结构的形成。氧化TGA结果表明,合成的BN纳米结构在高于550oC的温度下具有热稳定性。通过IGA进行的储氢测量表明,BNNTs可以吸附0.85 wt%的氢,是商用CNT的两倍。 ud