Penelitian ini bertujuan untuk mengetahui kondisi optimum adsorpsi warna ekstrak cincau hijau menggunakan arang bambu (Gigantochloa verticillata) tercampur bentonit serta karakterisasinya. Arang bambu diaktivasi dengan larutan H3PO4 5%, 10% dan 15% serta pemanasan pada suhu 700oC selama 60 menit. Sedangkan bentonit diaktivasi menggunakan larutan HCl 5 N dengan pemanasan pada suhu 70oC. Preparasi ekstrak cincau hijau dilakukan dengan pelarut air dan metanol. Selanjutnya dilakukan pengontakkan adsorben dengan ekstrak cincau hijau. Adsorben sebelum dan sesudah kontak dikarakterisasi menggunakan instrumentasi FTIR (Fourier Transform Infrared Spectometer) dan analisis SEM (Scanning Electron Microscope). Arang bambu aktif yang diaktivasi dengan larutan H3PO4 5% memiliki daya adsorpsi (96,04%) dan randemen (58,2%) paling tinggi. Perbandingan optimum pada pencampuran arang bambu dan bentonit adalah 3:1. Kondisi optimum pengontakkan ekstrak cincau hijau dengan adsorben adalah pada konsentrasi adsorben 1,5% dan lama waktu kontak 10 menit. Hasil analisis FTIR menunjukkan bahwa adsorben yang telah dikontakkan dengan ekstrak cincau hijau tidak mengalami perubahan secara kimia. Sedangkan berdasarkan analisis SEM, adsorben sebelum dan sesudah pengontakkan tidak mengalami perubahan secara signifikan (pori-pori adsorben masih terbuka). ududKata kunci: Arang bambu, bentonit, ekstrak cincau hijau, adsorpsiududThe purpose of this research is to optimize condition in color adsorption of green cincau extract used bamboo charcoal (Gigantochloa verticillata) and bentonite with characterization. Bamboo charcoal activated with 5%, 10% and 15% H3PO4 solution and heated at temperature 700oC for 60 minutes. Whereas bentonite was activated with 5 N HCl solution and heated at temperature 70oC. Green cincau was extracted with water and metanol. And then the extract was contacted with adsorbent (bamboo charcoal and bentonite). Adsorbent pre and post contacts were characterized by fourier transform infrared (FTIR) and scanning electron microscope (SEM). Bamboo charcoal which activated by 5% H3PO4 solution has adsorption capacity (96,04%) and the highest randemen is 58,2%. Optimum ratio of bamboo charcoal and bentonite was 3:1. Optimum contacted condition green cincau extract with adsorbent were 1,5% adsorbent concentration and ten minutes contact time. The FTIR spectrum show that adsorben which contacted with green cincau extract did not change chemical characterization. According to SEM analysis, adsorbent pre and post contact did not change significantly (adsorbent pores not closed).udKeywords: Bamboo charcoal, bentonite, green cincau extract, adsorption
展开▼
机译：本研究旨在确定掺有膨润土的竹炭（Gigantochloa verticillata）对草冻提取物颜色吸附的最佳条件及其特性。竹炭用5％，10％和15％的H3PO4溶液活化，并在700oC加热60分钟。膨润土是通过5 N HCl溶液在70oC加热而活化的。用水和甲醇溶剂制备草冻提取物。然后用草胶提取物提取吸附剂。接触前后的吸附剂使用FTIR（傅立叶变换红外光谱仪）仪器和SEM（扫描电子显微镜）进行表征。用5％H3PO4溶液活化的竹炭具有最高的吸附能力（96.04％）和改性剂（58.2％）。混合竹炭和膨润土的最佳比例为3：1。使草胶提取物与吸附剂接触的最佳条件是吸附剂浓度为1.5％，接触时间为10分钟。 FTIR分析的结果表明，与绿草冻提取物接触的吸附剂没有化学变化。尽管基于SEM分析，但接触之前和之后的吸附剂没有显着变化（吸附剂孔仍然敞开）。关键词：竹炭，膨润土，绿草果冻提取物，吸附本研究的目的是优化使用表征的竹炭（Gigantochloa verticillata）和膨润土对绿草果冻提取物进行颜色吸附的条件。竹炭用5％，10％和15％的H3PO4溶液活化，并在700oC的温度下加热60分钟。膨润土用5 N HCl溶液活化并在70oC加热。用水和甲醇萃取草冻。然后将提取物与吸附剂（竹炭和膨润土）接触。吸附剂的前后接触通过傅里叶变换红外（FTIR）和扫描电子显微镜（SEM）进行表征。用5％H3PO4溶液活化的竹炭具有吸附能力（96.04％），最高收率为58.2％。竹炭和膨润土的最佳比例为3：1。吸附剂的最佳接触条件为草胶浸膏的吸附剂浓度为1.5％，接触时间为10分钟。 FTIR光谱表明，与绿草冻提取物接触的吸附剂没有改变化学特性。根据SEM分析，接触前后的吸附剂没有发生明显变化（吸附剂的孔未封闭） Ud关键字：竹炭，膨润土，绿草冻提取物，吸附
展开▼
