Fabrication of a working Bi-2223 superconducting magnet cooled by liquid nitrogen

摘要

A practical Bi-2223 superconducting magnet, working in liquid nitrogen (L.N2), was designed and fabricated. Bi-2223 tape with a critical current of 147 A was prepared by a controlled overpressure (CT-OP) process at 77.3 K in self-field. Ten double-pancake coils were resistively connected by copper terminals. The bore diameter was 54 mmphi, the magnet outer diameter was 122 mmphi, the height of the magnet was 124 mm, and the weight of the magnet was about 3 kg. The maximum magnetic field at the center of the bore was 0.48 T with an operating current of 50 A. The experimental results agree well with design predictions calculated by finite element method. AC operation was also performed, and no distortion of the voltage waveform was observed. Therefore, this Bi-2223 superconducting magnet is a suitable replacement for copper magnets designed for applications in science and technology.