General regularities in the failure kinetics of steel of main gas pipelines (17GS) are established using the method of complete stress-strain curves, meanwhile in-service degradation of metals is taken into account. The influence of material degradation on material properties under static tensioning is considered using two independent approaches: the phenomenological model of damage accumulation in metals, and the fractographic analysis method. The accumulation of in-service damage is found to increase a degree of material opening and lead to partial “embrittlement” of the steel matrix due to the microdefects accumulation in the vicinity of metal cracking caused by hydrogenation.