Tailoring Low-field Strain Properties of 0.97Bi1/2(Na0.78K0.22)1/2TiO3-0.03LaFeO3-Bi1/2(Na0.82K0.18)1/2TiO3 Lead-Free Relaxor/Ferroelectric Composites

摘要

We investigated the effect of Bi1/2(Na0.82K0.18)1/2TiO3 (BNKT) modification on the ferroelectric and electric-field-induced strain (EFIS) properties of lead-free 0.97Bi1/2(Na0.82K0.18)1/2TiO3-0.03LaFeO3 (BNKTLF) ceramics as a function of BNKT content (x= 0, 0.1, 0.2, 0.3, 0.5, and 1). BNKT-modified BNKTLF powders were synthesized using a conventional solid-state reaction method. As the BNKT content x increased from 0 to 1 the normalized electric-field-induced strain (Smax/Emax) was observed to increase at relatively low fields, i.e., below the poling field. Moreover, BNKTLF-30BNKT showed about 460 pm/V as low as at 3 kV/mm, which is a considerably high value among the lead-free systems reported so far. Consequently, it was confirmed that ceramic-ceramic composite, a mixture of an ergodic relaxor matrix and embedded ferroelectric seeds, is a salient way to make lead-free piezoelectrics practical with enhanced EFIS at low field as well as less hysterical.