Growth of Initial Clog Deposits during Continuous Casting of Ti-ULC Steel – Formation and Reduction of the Initial Deposits at Nozzle/Steel Interface

机译：连续铸造Ti-ULC钢的初始堵塞沉积物的生长 - 喷嘴/钢界面的初始沉积物的形成和减少

代理获取

本网站仅为用户提供外文OA文献查询和代理获取服务，本网站没有原文。下单后我们将采用程序或人工为您竭诚获取高质量的原文，但由于OA文献来源多样且变更频繁，仍可能出现获取不到、文献不完整或与标题不符等情况，如果获取不到我们将提供退款服务。请知悉。

页面导航

著录项
引文网络
相似文献
相关主题

著录项

作者
Joo-Hyeok Lee; Youn-Bae Kang;
展开▼
作者单位

展开▼
年度 2020
总页数
原文格式 PDF
正文语种
中图分类

相似文献

外文文献
中文文献
专利

1. Growth of Initial Clog Deposits during Continuous Casting of Ti-ULC Steel - Formation and Reduction of the Initial Deposits at Nozzle/Steel Interface [J] . Joo-Hyeok LEE, Youn-Bae KANG ISIJ international . 2020,第3期

机译：Ti-ULC钢连续铸造过程中初始堵塞物的生长-喷嘴/钢界面处初始沉积物的形成和减少
2. Growth of Initial Clog Deposits during Continuous Casting of Ti-ULC Steel – Formation and Reduction of the Initial Deposits at Nozzle/Steel Interface [J] . Joo-Hyeok Lee, Youn-Bae Kang ISIJ international . 2020,第3期

机译：Ti-ULC钢连续铸造过程中初始堵塞物的生长–喷嘴/钢界面处初始沉积物的形成和减少
3. Influence of Al/Ti Ratio in Ti-ULC Steel and Refractory Components of Submerged Entry Nozzle on Formation of Clogging Deposits [J] . Joo-Hyeok LEE, Myeong-Hun KANG, Sung-Kwang KIM, ISIJ international . 2019,第5期

机译：Ti-ULC钢中Al / Ti比和浸入式喷嘴的耐火成分对堵塞沉积物形成的影响
4. Study of Clogging Deposit Buildup in Al-killed and Ca-Treated High-Sulfur Steels With Focus on the Steel/Refractory Interface [C] . Philipp Dorrer, Susanne K. Michelic, Gerald Kloesch, Iron and Steel Technology Conference . 2017

机译：用焦点钢/耐火材料界面堵塞和CA-处理高硫钢堵塞沉积堆积的研究
5. Nozzle clogging during the continuous casting of aluminum-killed steel. [D] . Trueba, Luis, Jr. 2003

机译：铝镇静钢的连续铸造过程中喷嘴堵塞。
6. Formation of Surface Deposits on Steel and TitaniumAviation Fuel Tubes under Real Operating Conditions [O] . Igor Velkavrh, *, Ion Palamarciuc, 2019

机译：在钢和钛上形成表面沉积物实际操作条件下的航空燃油管
7. Development of Anti-clogging Immersion Nozzle (AI Nozzle) Technology for Continuous Casting of Steel [O] . Yuichi Tsukaguchi, Toru Kato, Shinsuke Watanabe, 2011

机译：钢连铸铸造抗堵塞浸没喷嘴（AI喷嘴）技术的研制
8. Criteria for the Formation of Cracks during Continuous Casting of Special Steels. Cost 504 Casting Technology Project SF 3. Final Report 1988-91. [R] . Holappa, L., Louhenkilpi, S., Miettinen, J. 1991

机译：特种钢连铸过程中裂纹形成的标准。成本504铸造技术项目sF 3.最终报告1988-91。

Growth of Initial Clog Deposits during Continuous Casting of Ti-ULC Steel – Formation and Reduction of the Initial Deposits at Nozzle/Steel Interface

著录项

引文网络

相似文献

相关主题

期刊订阅