Photoelectrochemical Behavior of a Molecular Ru-Based Water-Oxidation Catalyst Bound to TiO_2-Protected Si Photoanodes

摘要

A hybrid photoanode based on a molecular water oxidation precatalyst was prepared from TiO_2-protected n- or p+-Si coated with multiwalled carbon nanotubes (CNT) and the ruthenium-based water oxidation precatalyst [Ru^(IV)(tda)(py-pyr)_2(O)], 1(O) (tda^(2–) is [2,2′:6′,2″-terpyridine]-6,6″-dicarboxylato and py-pir is 4-(pyren-1-yl)-N-(pyridin-4-ylmethyl)butanamide). The Ru complex was immobilized by π–π stacking onto CNTs that had been deposited by drop casting onto Si electrodes coated with 60 nm of amorphous TiO_2 and 20 nm of a layer of sputtered C. At pH = 7 with 3 Sun illumination, the n-Si/TiO_2/C/CNT/[1+1(O)] electrodes exhibited current densities of 1 mA cm^(–2) at 1.07 V vs NHE. The current density was maintained for >200 min at a constant potential while intermittently collecting voltammograms that indicated that over half of the Ru was still in molecular form after O_2 evolution.