Mechanical Properties and Fire Resistance of Magnesium-Cemented Poplar Particleboard

摘要

Magnesium-cemented poplar particleboard (MCPB) is a new environmental inorganic magnesium cementitious composite without formaldehyde release. In this study, soybean flour (SM), silane coupling agent (KH560), soybean protein isolate (SPI), polyethylene glycol (PEG-400), maleic anhydride (MAH), and polyacrylic acid (PAA) were added to MCPB to improve the mechanical properties, waterproofing properties, and flame retardancy. The results show that the SPI group had the best mechanical performance; the modulus of elasticity (MOE) was up to 5192 MPa and exceeded the Chinese national standard GBT 4897-2015 (GBT) by 67.4%, the modulus of rupture (MOR) reached 17.72 MPa and exceeded GBT by 18%. Thickness swelling (TS) after 24-hour immersion was 0.29% and reached the standard of GBT (≤16%). The fire resistance test of MCPB indicated that the KH560 group improved the flame retardancy, the heat release rate (HRR) was 18kW/m2, the total smoke produced (TSP) was 0.192 m2, the total heat release (THR) was 29.71 MJ/kg, which reached the Chinese national standard GBT 8624-2012.