Perbandingan Hasil Pengoksidan Elektrokimia Etanol dalam Larutan Alkali yang Menggunakan Elektrod Platinum-Polivinilklorida (Pt-PVC) dan Kepingan Logam Pt = Comparison of Electrooxidation Yield of Ethanol in Alkaline Medium using Platinum-Polyvinyl chloride (Pt-PVC) and Pt Metal Foil Electrodes

摘要

A modification of platinum-polyvinyl chloride (Pt-PVC) electrode for the electrooxidation of ethanol in alkaline solutionudhas been investigated. Pt-PVC electrode was prepared by mixed together platinum metal powder with PVC (95:5 w/w),udhomogenized, added with tetrahydrofuran to dissolved the dried, put into 1 cm diameter mould and press at 10 ton/cm2.udStudies on electrochemicals behavior for Pt-PVC electrode were carried out using cyclic voltammetry and chronocoulometryudmodes. The higher current density for hydroxide adsorption peak were recorded, 0.25 mA/cm2 and 85 mA/cm2 respectivelyudwhen Pt-PVC electrode was used compared to Pt electrode. This indicates that Pt-PVC electrode gives better conductivityudand electrochemical behavior to electrooxidation of ethanol in KOH compared to Pt electrode. Result obtained shows theudused of Pt-PVC electrode for electrooxidation of 0.25 M ethanol in 1.0 M KOH supporting electrolyte increased theudpercentage of acetic acid produced compared to Pt electrode.