首页> 外文OA文献 >Investigation of the Erosion Damage Mechanism and Erosion Prediction of Boronized Coatings at Elevated Temperatures

【2h】

Investigation of the Erosion Damage Mechanism and Erosion Prediction of Boronized Coatings at Elevated Temperatures

机译：升高温度下硼化涂层侵蚀损伤机理及侵蚀预测的研究

代理获取

本网站仅为用户提供外文OA文献查询和代理获取服务，本网站没有原文。下单后我们将采用程序或人工为您竭诚获取高质量的原文，但由于OA文献来源多样且变更频繁，仍可能出现获取不到、文献不完整或与标题不符等情况，如果获取不到我们将提供退款服务。请知悉。

页面导航

著录项
引文网络
相似文献
相关主题

著录项

作者
Liu-Xi Cai; Yun Li; Shun-Sen Wang; Yao He; Fang Li; Ze-Kun Liu;
展开▼
作者单位

展开▼
年度 2020
总页数
原文格式 PDF
正文语种
中图分类

相似文献

外文文献
中文文献
专利

1. Degradation mechanisms of aluminium diffusion coatings on 12 percent chromium steels under elevated temperature erosion-oxidation conditions [J] . E. Huttunen-Saarivirta, F.H. Stertt, V. Rohr Materials at High Temperatures . 2006,第1期

机译：高温侵蚀-氧化条件下12％铬钢上铝扩散涂层的降解机理
2. An investigation on erosion behavior of nanostructured 7YSZ coatings at elevated temperature [J] . Qu Zhaoliang, Cheng Xiangmeng, Wu Jingen, Surface & Coatings Technology . 2016,第Null期

机译：纳米结构7YSZ涂层在高温下的腐蚀行为研究
3. A comparison of elevated temperature erosion resistance of four new HVCC coatings with other wire sprayed coatings [J] . B.Q. Wang Journal of Materials Processing Technology . 2004,第0期

机译：四种新型HVCC涂层与其他钢丝喷涂涂层的耐高温腐蚀性能比较
4. Investigation of elevated temperature erosion mechanisms and erosion behavior of Waspaloy (superalloy) under hot air jet conditions [C] . K. G. Thirugnanasambantham, M. Pankajrishikesh, I. G. Vishal, International Conference on Recent Trends in Mechanical and Materials Engineering . 2020

机译：热风射流条件下蜂马（超合金）温度腐蚀机理和侵蚀行为的研究
5. Investigation of the Degradation Mechanisms of Particulate Reinforced Epoxy Coatings and Zinc-Rich Coatings Under an Erosion and Corrosion Environment for Oil and Gas Industry Applications [D] . Wang, Dailin. 2017

机译：石油和天然气工业在腐蚀和腐蚀环境下颗粒增强环氧涂料和富锌涂料的降解机理研究
6. Numerical Investigation of Temperature Distribution in an Eroded Bend Pipe and Prediction of Erosion Reduced Thickness [O] . Hongjun Zhu, Guang Feng, Qijun Wang -1

机译：弯曲弯管内温度分布的数值研究及减薄厚度的预测
7. Erosion Resistance and Damage Mechanism of TiN/ZrN Nanoscale Multilayer Coating [O] . Jiao Chen, Mingrui Geng, Yuqin Li, 2019

机译：锡/ ZrN纳米尺度多层涂层的耐腐蚀性和损伤机理
8. Investigation of Fatigue Damage Mechanisms in a Metal Matrix Composite Under Elevated Temperature. [R] . Portner, B. D. 1990

机译：高温下金属基复合材料疲劳损伤机理研究。

Investigation of the Erosion Damage Mechanism and Erosion Prediction of Boronized Coatings at Elevated Temperatures

著录项

引文网络

相似文献

相关主题

期刊订阅