Magnesium forms 2% in the earth's crust, magnesium is widely used in industry. For example, industrial machinery and electronics, and many developed in the field of biomedicine, especially in the field of orthopedics. Magnesium about 60% is present in the human bones, therefore it has great potential for human body implants. However, it is necessary to increase the mechanical and chemical properties of magnesium in order to be used for bone implant materials. Production process using squeeze casting method. Through this method, Liquid metal is given hydraulic pressure, so the mechanical properties of magnesium were better. In this research use temperature parameter = 450?C, pressure = 300 MPa, duration of press 1 minute and variation of holding time 7 and 9 minutes. Magnesium AZ31 increased compared with samples without treatment. Tensile strength with holding time 7 minutes equal to120.27 MPa, holding time 9 minutes was 128.77 MPa, and samples without treatment of was 94.63 MPa. The magnesium hardness value of AZ31 decreased at 7 minute detention was 39 VHN, compared with the sample without treatment of was 41.8 VHN. And the hardness value increased at holding time 9 minutes equal to 46.2 VHN. However, it should be noted that excessive overheating and holding time may lead to decrease in magnesium mechanical properties of AZ31.Magnesium membentuk 2% pada kerak bumi, magnesium banyak digunakan pada industri. Misalnya, industri mesin dan elektronik, dan banyak dikembangkan pada bidang biomedik, terutama di bidang orthopedi. Magnesium sekitar 60% ada pada tulang manusia, oleh karna itu berpotensi besar untuk implan tubuh manusia. Namun, diperlukan peningkatan sifat mekanik dan kimia magnesium agar dapat digunakan untuk bahan implan tulang. Proses produksi menggunakan metode pengecoran tekan. Melalui metode ini, logam cair diberi tekanan hidrolik, sehingga sifat mekanik magnesium lebih baik. Dalam penelitian ini menggunakan parameter temperatur = 450?C, tekanan = 300 MPa, durasi tekan 1 menit dan variasi holding time 7 dan 9 menit. Magnesium AZ31 meningkat dibandingkan sampel tanpa perlakuan. Kekuatan tarik dengan holding time 7 menit sebesar 120,27 MPa, holding time 9 menit sebesar 128,77 MPa, dan sampel tanpa perlakuan sebesar 94,63 MPa. Nilai kekerasan magnesium AZ31 menurun pada holding time 7 menit sebesar 39 VHN, bila dibandingkan sampel tanpa perlakuan sebesar 41,8 VHN. Dan nilai kekerasan meningkat pada holding time 9 menit sebesar 46,2 VHN. Namun, perlu diperhatikan pemanasan dan holding time yang berlebih (over heat) dapat mengakibatkan penurunan sifat mekanik magnesium AZ31.
展开▼
机译：镁在地壳中形成2％，镁在工业中广泛应用。例如，工业机械和电子产品，许多在生物医学领域开发，特别是在骨科领域。在人体骨骼中存在约60％的镁，因此它具有很大的人体植入物的潜力。然而，有必要增加镁的机械和化学性质，以便用于骨植入材料。采用挤压铸造法生产工艺。通过这种方法，液态金属是液压，因此镁的机械性能更好。在本研究中，使用温度参数= 450？C，压力= 300MPa，按压1分钟的持续时间和保持时间7和9分钟的变化。与无需处理的样品相比，镁AZ31增加。保持时间7分钟等于120.27MPa的拉伸强度，保持时间9分钟为128.77MPa，并且在不处理的样品为94.63MPa。 AZ31的镁硬度值在7分钟的滞留时下降为39 VHN，与样品相比，无需治疗为41.8 VH。并且硬度值在保持时间9分钟等于46.2 VH时增加。然而，应该注意，过度过热和保持时间可能导致AZ31的镁力学性能降低。Membentuk 2％Pada Kerak Bumi，Magneium Banyak Digunakan Pada Industri。 Misalnya，Industi Mesin Dan Elektronik，Dan Banyak Dikembangkan Pada Bidang Biomedik，Terutama di Bidang Orthopedi。镁Sekitar 60％Ada Pada Tulang Manusia，Oleh Karna Itu Berpotensi Besar Untuk Implan Tubuh Manusia。南村，迪伯朗彭彭丹皮特Mekanik Dan Kimia Magnesium Agar Dapat Digunakan Untuk Bahan Implan Tulang。漂泊Produksi Menggunakan Metode PengeCoran Tekan。 Melalui Metode Ini，Logam Cair Diberi Tekanan Hidrolik，Seingga Sifat Mekanik Magnesium Lebih Baik。达拉姆彭利安ini menggunakan参数温度= 450？c，tekanan = 300 mpa，durasi tekan 1 menit dan variasi持有时间7 dan 9 menit。 Magnesium AZ31 Meningkat Dibandingkan Sampel Tanpa Perlakuan。 Kekuatan Tarik Dengan持有时间7 Menit Sebesar 120,27 MPa，持有时间9梅特Sebesar 128,77 MPa，Dan Sampel Tanpa Perlakuan Sebesar 94,63 MPa。 Nilai Kekerasan Magnesium AZ31 Menurun Pada持有时间7 Menit Sebesar 39 VHN，Bila Dibandingkan Sampel Tanpa Perlakuan Sebesar 41,8 Vhn。 Dan Nilai Kekerasan Meningkat Pada举行时间9钟线Sebesar 46,2 VHN。南村，菲尔卢·普勒希特尼克望着时间杨伯利（在热）Dapat Mengakibatkan Penurunan Sifat Mekanik镁AZ31。
展开▼