Influence of heat treatment on the structure and properties of polyamide 6/ halloysite nanocomposites

摘要

The nanocomposites of polyamide 6 (PA6) with halloysite nanotubes (HNT) were prepared by extrusion using co-rotating twin-screw extruder and then the standard test specimens were injected using a screw injection moulding machine. The content of HNT in the nanocomposites was 5 or 10 weight percent. The heat treatment of unmodified PA6 and nanocomposites was carried out in silicone oil in temp. 150±2°C. The samples were annealed for 3 hours and then cooled at a rate of 4 K/min. Differential scanning calorimetry (DSC) causes annealing to increase the crystallinity of the polyamide matrix. After an annealing treatment a nanocomposite with better mechanical properties was obtained. Halloysite nanotubes in polyamide matrix play the role of a nucleating agent.