Preparation and Characterization of Urea Formaldehyde @ Epoxy Resin Microcapsule on Waterborne Wood Coatings

摘要

Urea formaldehyde @ epoxy resin microcapsules were prepared by two steps in situ polymerization, and the morphology and composition of microcapsules with different mass ratios of core to wall material were examined by scanning electron microscopy (SEM) and infrared (IR) spectroscopy. The microcapsules were added to the waterborne wood coatings to explore the effect of microcapsules on the properties of coatings and their self-repairing characteristics, and the gloss, hardness, adhesion, and impact resistance of the waterborne wood coatings were investigated. The results showed that when the concentration of microcapsule was 10.0% and the mass ratio of core to wall material was 0.83:1, the waterborne wood coatings had a good comprehensive performance and less negative impact. In the scratch test, the waterborne wood coatings with a concentration of 10.0% microcapsule had good repair ability. The possibility of applying the self-repairing technology of microcapsule to waterborne wood coatings was discussed through the preparation and performance characterization of self-repairing coatings and the results can become a guideline for the engineering application of waterborne wood coatings.