首页> 外文OA文献 >The interaction of corrosion fatigue and stress-corrosion cracking in a precipitation-hardened martensitic stainless steel

【2h】

The interaction of corrosion fatigue and stress-corrosion cracking in a precipitation-hardened martensitic stainless steel

机译：沉淀硬化马氏体不锈钢中腐蚀疲劳和应力腐蚀开裂的相互作用

代理获取

本网站仅为用户提供外文OA文献查询和代理获取服务，本网站没有原文。下单后我们将采用程序或人工为您竭诚获取高质量的原文，但由于OA文献来源多样且变更频繁，仍可能出现获取不到、文献不完整或与标题不符等情况，如果获取不到我们将提供退款服务。请知悉。

页面导航

著录项
引文网络
相似文献
相关主题

著录项

作者
J. Ryan Donahue; Amber B. Lass; James T. Burns;
展开▼
作者单位

展开▼
年度 2017
总页数
原文格式 PDF
正文语种
中图分类

相似文献

外文文献
中文文献
专利

1. The interaction of corrosion fatigue and stress-corrosion cracking in a precipitation-hardened martensitic stainless steel [J] . J. Ryan Donahue, Amber B. Lass, James T. Burns NPJ Materials Degradation . 2017,第1期

机译：沉淀硬化马氏体不锈钢中腐蚀疲劳与应力腐蚀开裂的相互作用
2. Fatigue crack propagation under gaseous hydrogen in a precipitation-hardened martensitic stainless steel [J] . Z. Sun, G. Benoit, C. Moriconi, International journal of hydrogen energy . 2011,第14期

机译：沉淀硬化马氏体不锈钢在气态氢作用下的疲劳裂纹扩展
3. Modelling of corrosion fatigue crack initiation on martensitic stainless steel in high cycle fatigue regime [J] . El May Mohamed, Saintier Nicolas, Palin-Luc Thierry, Corrosion science . 2018,第APRa期

机译：高循环疲劳状态下马氏体不锈钢腐蚀疲劳裂纹萌生建模
4. HYDROGEN ASSISTED FATIGUE CRACK GROWTH IN A PRECIPITATION-HARDENED MARTENSITIC STAINLESS STEEL UNDER GASEOUS HYDROGEN [C] . Giovambattista Bilotta, Mandana Arzaghi, Gilbert Henaff, ASME Pressure Vessels and Piping conference . 2014

机译：气态氢作用下析出硬化马氏体不锈钢中氢的疲劳裂纹扩展
5. Mechanistic studies of stress-corrosion cracking in austenitic stainless steels and in copper-zinc alloys. [D] . Wu, Xiaozhu. 1998

机译：奥氏体不锈钢和铜锌合金中应力腐蚀开裂的机理研究。
6. A Comparative Study of Localized Corrosion and Stress Corrosion Cracking of 13Cr Martensitic Stainless Steel Using Acoustic Emission and X-ray Computed Tomography [O] . Kaige Wu, Kaita Ito, Ippei Shinozaki, 2019

机译：13Cr马氏体不锈钢的声发射与X射线计算机断层扫描技术比较研究局部腐蚀和应力腐蚀开裂
7. The nature, detection, and prevention of intergranular corrosion in 18 Cr-8 Ni stainless steel: stress-corrosion cracking in 18 Cr-8 Ni austenitic stainless steel ; 18 Cr-8 Ni stainless steel in high temperature service. [O] . Tuthill Arthur Horace 1946

机译：18 Cr-8 Ni不锈钢的晶界腐蚀的性质，检测和预防：18 Cr-8 Ni奥氏体不锈钢的应力腐蚀开裂； 18 Cr-8 Ni不锈钢在高温下使用。

The interaction of corrosion fatigue and stress-corrosion cracking in a precipitation-hardened martensitic stainless steel

著录项

引文网络

相似文献

相关主题

期刊订阅