Influence of plasma exposures on tungsten behavior was studied in QSPA Kh-50 facility and pulsed plasma gun PPA.udPlasma loads were chosen either below the melting threshold or resulting in pronounced melting. Evolution of residualudstresses and lattice spacing was studied for various number of hydrogen or helium plasma impacts. The value of residualudstresses depends on irradiation dose and kind of impact plasma. The non monotone change of lattice spacing was observedudfor melted surface. The damage of exposed surface was caused by cracks appearing.