首页> 外文OA文献 >Mechano-Chemical Polishing of Alloy 600 for Accelerated Crack Initiation in Simulated PWR Primary Water Environment and Three-Dimensional Crystallographic Characterization

【2h】

Mechano-Chemical Polishing of Alloy 600 for Accelerated Crack Initiation in Simulated PWR Primary Water Environment and Three-Dimensional Crystallographic Characterization

机译：合金600的机械化学抛光，用于模拟PWWR初级水环境中加速裂纹启动及三维晶体特征

代理获取

本网站仅为用户提供外文OA文献查询和代理获取服务，本网站没有原文。下单后我们将采用程序或人工为您竭诚获取高质量的原文，但由于OA文献来源多样且变更频繁，仍可能出现获取不到、文献不完整或与标题不符等情况，如果获取不到我们将提供退款服务。请知悉。

页面导航

著录项
相似文献
相关主题

著录项

作者
Ki-Taek Jung; Hiroaki Tsuchiya; Shinji Fujimoto;
展开▼
作者单位

展开▼
年度 2020
总页数
原文格式 PDF
正文语种
中图分类

相似文献

外文文献
中文文献
专利

1. Mechano-Chemical Polishing of Alloy 600 for Accelerated Crack Initiation in Simulated PWR Primary Water Environment and Three-Dimensional Crystallographic Characterization [J] . Jung Ki-Taek, Tsuchiya Hiroaki, Fujimoto Shinji Materials transactions . 2020,第7期

机译：合金600的机械化学抛光，用于模拟PWWR初级水环境中加速裂纹启动及三维晶体特征
2. Crack growth and cracking behavior of Alloy 600/182 and Alloy 690/152 welds in simulated PWR primary water [J] . Yun Soo Lim, Dong Jin Kim, Sung Woo Kim, Nuclear engineering and technology . 2019,第1期

机译：合金600/182和690/152合金焊缝在模拟PWR初级水中的裂纹扩展和开裂行为
3. Microstructural characterization on intergranular stress corrosion cracking of Alloy 600 in PWR primary water environment [J] . Yun Soo Lim, Hong Pyo Kim, Seong Sik Hwang Journal of Nuclear Materials: Materials Aspects of Fission and Fusion . 2013,第1a3期

机译：压水堆一次水环境中600合金晶间应力腐蚀开裂的组织特征
4. Crystallographical Characterization of Initiation of Intergranular Stress Corrosion Cracking of Alloy 600 in PWR Environment [C] . Shinji Fujimoto, Masahito Mochizuki, Yuya Morita, International conference on environmental degradation of materials in nuclear power systems-water reactors . 2012

机译：压水堆环境下合金600晶间应力腐蚀开裂的结晶学表征
5. Indications of Stress Corrosion Cracking Resistance in Alloy 82 Dissimilar Metal Welds in Simulated Primary Water Environments [D] . Persaud, Suraj 2011

机译：模拟的一次水环境中82合金异种金属焊缝的耐应力腐蚀开裂迹象
6. Stress Corrosion Behaviors of 316LN Stainless Steel in a Simulated PWR Primary Water Environment [O] . Yong Huang, Weisong Wu, Shuo Cong, 2018

机译：316LN不锈钢在模拟压水堆原水环境中的应力腐蚀行为
7. Electrochemical Properties of Oxide Films Formed on Cold Worked Alloy600 and Alloy690 in Simulated PWR Primary Water Environments [O] . Whee-Sung Kim, Hiroaki Tsuchiya, Masugu Sato, 2015

机译：在仿真PWWR初级水环境中在冷加工合金600和合金690上形成的氧化膜的电化学性能

Mechano-Chemical Polishing of Alloy 600 for Accelerated Crack Initiation in Simulated PWR Primary Water Environment and Three-Dimensional Crystallographic Characterization

著录项

相似文献

相关主题

期刊订阅