A glucose biosensor based on novel Lutetium bis-phthalocyanine incorporated silica-polyaniline conducting nanobeads

摘要

The facile preparation of highly sensitive electrochemical bioprobe based on lutetium 13 phthalocyanine incorporated silica nanoparticles (SiO2(LuPc2)) grafted with Poly(vinyl 14 alcohol-vinyl acetate) itaconic acid (PANI(PVIA)) doped polyaniline conducting nanobeads 15 (SiO2(LuPc2)PANI(PVIA)-CNB) is reported. The preparation of CNB involves two stages (i) 16 pristine synthesis of LuPc2 incorporated SiO2 and PANI(PVIA); (ii) covalent grafting of 17 PANI(PVIA) onto the surface of SiO2(LuPc2). The morphology and other physico-chemical 18 characteristics of CNB were investigated. The scanning electron microscopy images show 19 that the average particle size of SiO2(LuPc2)PANI(PVIA)-CNB was between 180-220 nm. 20 The amperometric measurements showed that the fabricated SiO2(LuPc2)PANI(PVIA)-21 CNB/GOx biosensor exhibited wide linear range (1-16 mM) detection of glucose with a low 22 detection limit of 0.1 mM. SiO2(LuPc2)PANI(PVIA)-CNB/GOx biosensor exhibited high 23 sensitivity (38.53 μA mM−1 cm−2) towards the detection of glucose under optimized 24 conditions. Besides, the real (juice and serum) sample analysis based on a standard addition 25 method and direct detection method showed high precision for measuring glucose at 26 SiO2(LuPc2)PANI(PVIA)-CNB/GOx biosensor. The SiO2(LuPc2)PANI(PVIA)-CNB/GOx 27 biosensor stored under refrigerated condition over a period of 45 days retains ~ 96.4 % 28 glucose response current.