Thickness dependent competing magnetic anisotropy energies were investigated to explore the global magnetic behaviours of FineMET amorphous thin films. A dominant perpendicular magnetization component in the as-deposited state of thinner films was observed due to high magnetoelastic anisotropy energy which arises from stresses induced at the substrate-film interface. This perpendicular magnetization component decreases with increasing film thickness. Thermal annealing at elevated temperature revealed a significant influence on the magnetization state of the FineMET thin films and controlled annealing steps leads to ultra-soft magnetic properties, making these thin films alloys ideal for a wide range of applications.