ZnTe/GaAs(2 1 1)B heterojunction valence band discontinuity measured by X-ray photoelectron spectroscopy

摘要

Thin ZnTe layers were grown by molecular beam epitaxy on single crystal GaAs(2 1 1)B substrates. Reflection high energy electron diffraction monitored the deoxidation of substrate and entire growth process. Valence band offset was calculated with X-ray photoelectron spectroscopy. Also interface formation of the ZnTe/GaAs was studied. Analysis shows that interface is abrupt and calculated valance band offset is 0.25±0.1 eV and indicates type I alignment. The experimental result agrees well with the theoretical predictions involving interface dipole effect as well as electron affinity rule.