Boundary Lubrication of Formulated C-Ether in Air to 300 Deg C. 1 Phosphorus Ester Additives.

摘要

Friction and wear measurements were made on CVM M-50 steel lubricated with three C-ether (modified polyphenyl ether) formulations in dry and wet air. Results were compared to those obtained with a formulated Type 2 ester and the C-ether base fluid. A ball-on-disk sliding friction apparatus was used. Experimental conditions were a 1-kilogram load, a 17-meter-per-minute (100-rpm) surface speed, and a 25 to 300 C (77 to 572 F) disk temperature range. The C-ether base fluid and the three formulated C-ether fluids yielded lower wear than the Type 2 ester over the entire temperature range. All C-ether fluids exhibited slightly higher friction coefficients than the ester from 150 to 300 C (302 to 572 F) and similar values from 25 to 150en1 C (77 to 302 F). In general, lower wear rates were observed with the C-ethers when tested in wet air as compared to a dry air atmosphere. (Author)