Graphite Fiber Polyimide Composites for Spherical Bearings to 340 C (650 F)

摘要

Journal bearings with self-alining spherical elements of graphite-fiber-reinforced-polyimide composites were tested from 24 to 340 C (75 to 650 F) at unit loads up to 3.5 times 10 to the 7th power N/sq m (5000 psi). The journal oscillated in the cylindrical bore of the composite element + or - 15 deg at 1 hertz. Outer races and journals were metal hardened of Rockwell C-32 and finished to 10 to the minus 7th power m. A 45 wt. percent graphite-fiber composite gave low friction (0.08 to 0.13), low wear, and almost no plastic deformation under any of the test conditions. Composites with 15 and 25 wt. percent graphite fiber failed by plastic deformation at 315 C (600 F) and 3.5 times 10 to the 7th power N/sq m (5000 psi). A composite with 60 wt. percent graphite fiber failed by brittle fracture under the same conditions, but had very low friction coefficients (0.05 to 0.10) and may be a good bearing material at lighter loads. (Author)