Dispersion-Strengthened Nickel-Alumina Alloy Produced from Comminuted Powders

摘要

An investigation was conducted to determine whether a nickel - 2-volume-percent alumina dispersion-strengthened material with a fine, uniformly distributed dispersoid could be produced, which was equivalent in short time tensile strength to commercially available thoriated sheet materials. Comminution and blending with a modified triple stirrer attritor and a hydrogen and vacuum precleaning treatment prior to consolidation were used. A product with a fine dispersoid with an average particle size of 0.04 micron and inution and blending with a modified triple stirrer attritor and a hydrogen and vacuum precleaning treatment prior to consolidation were used. A product with a fine dispersoid with an average particle size of 0.04 micron and an interparticle spacing of 0.7 micron was achieved. This material has a 1093 C (2000 F) short time tensile strength of 117 MN/sq m (16 900 psi). (Author)