Characterizations of four specimens processed as a part of the M553 sphere forming experiment performed during the Skylab 1 and 2 flight

摘要

Four specimens identified as SL-1.3, SL-1.8, SL-1.9 and SL-2.5 were submitted for metallurgical characterization. These specimens had been processed in the M512 Facility as a part of the M553 Sphere Forming Experiment performed during the Skylab 1/2 flight. Three of these specimens, SL-1.3, SL-1.8, and SL-2.5 were designed to be melted completely by the electron beam and detach themselves from their support posts and resolidify while floating free in the near zero gravity and vacuum environment of space. Specimens SL-1.3 and SL-1.8 were completely melted, but it is believed they did not leave their posts before solidifying. Specimen SL-2.5 was only partially melted. Specimen SL-1.9 was to be completely melted and retained on a large sting which was accomplished as planned. The nominal composition of the four specimens was: (1) SL-1.3 - Ni 12% Sn; (2) SL-1.8 - Ni 30% Cu; (3) SL-1.9 - Pure Ni; and (4) SL-2.5 - Pure Ni. These four specimens have been examined according to the Phase B Characterization Plan. The results are discussed and compared with similar characterization analyses run on ground base specimens.