Friction and wear of tin and tin alloys from minus 100 C to 150 C

摘要

Sliding friction experiments were conducted with an iron (110) single-crystal pin sliding on single and polycrystalline tin and tin alloys. Specimens were examined at various ambient temperatures from -100 to 150 C. Applied loads varied from 1 to 50 grams, and sliding velocity was constant at 0.7 mm/min. Results indicate that the crystal transformation of tin influences the friction coefficient. Friction was higher for the diamond structure (gray tin) than it was for the body-centered tetragonal structure (white tin). Bismuth arrested the crystal transformation, which resulted in constant friction over the temperature range -100 to 150 C. Both copper and aluminum enhanced the kinetics of transformation, with aluminum producing a nearly twofold change in friction with the crystal transformation.