Further Study of Near Solidus Intergranular Cracking in Inconel 718

摘要

A series of tests, performed to determine the strain necessary to initiate intergranular cracking in Inconel 718 as a function of temperature, contained enough scatter near the melting temperature that questions remained as to the best curve of curves to fit to the data. Fracture surface analysis showed that the scatter was due to incipient melting in the grain boundary region. The melting contributed to low fracture strain but had only a small on the incipient cracking strain. Gleeble tests, which could be interrupted by water quenching, were used to study the incipient intergranular melting of Inconel 718. This modified weld simulation test provided a sufficiently rapid quench to preserve the intergranular microstructure created during incipient melting. This structure was studied both microscopically and with energy dispensive X-ray analysis. The implications of incipient melting and low-strain incipient cracking on the development of microfissuring envelopes are discussed.