Crystal Nucleation in Glass-Forming Alloy and Pure Metal Melts under Containerless and Vibrationless Conditions

摘要

The undercooling behavior of large spheroids of Pd40Ni40P40 was investigated. By surface etching, supporting the specimens on a fused silica substrate, and successive heating and cooling, crystallization can be eliminated, presumable due to the removal of surface heterogeneities. By this method samples up to 3.2g with a 0.53 mm minor diameter, were made entirely glassy, except for some superficial crystals comprising less than 0.5% of the volume. These experiments show that a cooling rate of approximately 1 K/sec is adequate to avoid copious homogeneous nucleation in the alloy, and that by eliminating or reducing the effectiveness of heterogeneous nucleation sites, it is possible to form bulk samples of this metallic glass with virtually unlimited dimensions.