An Improved Technique for the Preparation of Mounted or Unmounted Carbon/Epoxy Specimens

摘要

As carbon/epoxy materials became more prevalent in the aerospace industry, microstructural analysis demanded specimen preparation techniques that led to better polished surfaces, achievable in a shorter time, and using fewer steps. The desire to use image analysis for material characterization also helped drive the goal for defect free surfaces. At NASA-Langley (LaRC), carbon/epoxy specimens had been historically prepared in 1 inch diameter Bakelite mounts. Carbon/epoxy specimens that were 1/8 to 1/4 inch thick were not affected by the heat and pressure required for mounting in Bakelite, however thinner specimens were crushed during mounting. A two-part room temperature curing epoxy was chosen as an alternative but sometimes voids developed between the specimen and the mounting material. This was prevented by either heating the epoxy to 140 degrees F to lower the viscosity of the epoxy or by using a vacuum impregnation apparatus. Both techniques helped facilitate flow and allowed the epoxy to penetrate crevices.