Investigation of the effect of thermal exposure on the mechanical properties of titanium/SiC composites

摘要

The objective was to evaluate the influence of thermal exposure, both isothermal and cyclic, on the reaction kinetics, mechanical properties and fracture behavior of Ti-1100 alloy/SiC fiber composites. Previously, it was determined that composites made with TiB2 coated SiC fiber (sigma) reacted at the same rate as SCS-6 fibers. As a result, the thinner surface coating on the Sigma fiber was completely consumed at shorter times than that on the SCS-6. Thermal cycling experiments were conducted on longitudinal and transverse Ti-1100/SCS-6 composites over a temperature range of 150 to 800 C for 500 cycles. The thermal exposures were carried out in air and argon. No appreciable tensile strength degradation was observed for samples cycled in argon, although a strength loss was noted for the samples cycled in air. Fracture surfaces characterization showed brittle matrix failure in regions near the surface and in regions where there was a path for O2 ingress.