Chemical Compatibility Issues Related to Use of Copper as an Interfacial Layerfor SiC Fiber Reinforced Ti3Ai+NB Composite

摘要

The reaction of Cu, a potential interfacial compliant layer for the Ti3Al plusNb/SiC composite, with SiC, SCS-6 fiber, and the Ti3Al plus Nb matrix was examined at two temperatures: 1223 and 1273 K. Reaction of Cu with SiC resulted in the formation of a CuSi solution and free carbon, the reaction product being molten at 1273 K. Hot pressing the SCS-6 fiber in a Cu matrix at 1273 K resulted in cracking and delamination of the outer carbon-rich coating, thus allowing the Cu to penetrate to the SiC-carbon coating interface and react with SiC. In contrast, no such damage to the outer coating was observed at 1223 K. There was excessive reaction between Cu and the Ti3Al plus Nb matrix, the reaction product being molten both at 1223 and 1273 K. An interlayer of Nb between Cu and Ti3Al plus Nb matrix prevented the reaction between the two.