Fracture Tests on Thin Sheet 2024-T3 Aluminum Alloy for Specimens with and Without Anti-Buckling Guides

摘要

A series of fracture test were conducted to determine the effects of specimen type specimen width and buckling on the fracture behavior of cracked thin sheet (0.063 inch thick) 2024-T3 aluminum alloy. A summary of the experimental measurements is presented for fracture tests conducted on two specimen types and various widths. Middle-crack tension M(T) and compact tension C(T) specimens were tested in the L-T and T-L orientation with duplicate tests for each condition. Four widths (W= 3, 12, 24, and 40 inch) were tested for the middle-crack tension specimens, and three widths (W=2, 4, and 6 inch) were tested for the compact tension specimens. The M(T) specimens were tested in either a constrained (out-of-plane displacements restrained with antibuckling guides) or unconstrained conditions were the specimen was free to buckle out of plane Measurements were made of load against crack extension for all specimens.