Magnetomechanical damping in cryogenic TbDy

摘要

Vibration damping in polycrystalline TbDy alloys was studied at cryogenic temperatures. The material was prepared by cold-rolling to induce crystallographic texture, and was then heat-treated to relieve internal stress. Mechanical hysteretic losses were measured at various strains, frequencies, and loading configurations at 77 K. Some textured TbDy materials demonstrated 22.6 energy dissipation in mechanical measurements at low frequency (0.01 Hz) and a mean logarithmic decrement of 0.23 at a higher frequency (25 kHz). Ultrasonic velocities of longitudinal and shear elastic waves were measured on single and polycrystalline TbDy; little variation in ultrasonic velocities was found evenfor samples with large variation in crystallographic texture and magnetomechanical properties.