Transition of PS300 Solid Lubricant Coating Technology to Field Aided by Demonstration on Key Substrate Alloys.

摘要

PS300 is a high-temperature solid lubricant coating originally developed to lubricate nickel-based superalloy shafts operating against foil air bearings in Oil-Free turbomachinery applications. PS300 is a plasma-spray-deposited coating developed at the NASA Glenn Research Center. It is available for non-exclusive licensing and has found applications in aerospace and industry. PS300 reduces friction and wear from below room temperature to over 650 C in both oxidizing and reducing environments. Early development centered on coating nickel-based shafts for use in turbomachinery. Potential industrial and aerospace customers, however, expressed interest in using the coating on a wide variety of substrates including steels, stainless steels, and nonferrous alloys like aluminum and titanium. To support this interest, a research program was carried out at Glenn in which nine different substrate candidate materials were evaluated for suitability with the PS300 coating. The materials were first coated with PS300 and then tested for coating strength and adhesion both before and after exposure to high-temperature air.