首页> 美国政府科技报告 >Studies of interdiffusion and alloy formation in Fe/V multilayers using hydrogen as a local probe
【24h】

Studies of interdiffusion and alloy formation in Fe/V multilayers using hydrogen as a local probe

机译:用氢作为局部探针研究Fe / V多层膜中的相互扩散和合金形成

获取原文

摘要

The thermal stability of Fe/V multilayers has been investigated for annealing temperatures in the range 423-650 K. The results show that the chemical composition profile is stable at 423 K. At higher temperatures, interdiffusion starts. No preferential alloy formation was found at the interfaces up to 650 K. The hydrogen concentration is measured with the (sup 1)H((sup 15)N, (alpha)(gamma))(sup 12)C-nuclear resonance reaction. 2 figs., 13 refs. (Atomindex citation 26:052161)