J-Integral characterization of the nozzle steels from intermediate test vessels IV-5 and IV-9

摘要

Reported here are the results of elastic-plastic fracture toughness tests performed on low alloy steels from the nozzles of the intermediate test vessels IV-5 and IV-9 from the Heavy Steel Section Technology Program at Oak Ridge National Laboratory. These vessels had been given prototypic nozzle corner flaw tests prior to the development of the ASTM E-813 standard test procedure for J-integral testing. The objective of this work is to provide J-integral material test support for future elastic-plastic fracture mechanics analysis of the nozzles. J-integral tests at 88(degrees)C (190(degrees)F) of the IV-5 nozzle material produced stable ductile tearing. The tearing resistance data are expected to support analysis of the observed similar stable tearing response of the nozzle corner flaw. J-integral tests at 24(degrees)C (75(degrees)F) of the IV-9 nozzle produced elastic-plastic fracture instability preceded by stable tearing. A similar response was observed in the IV-9 nozzle corner flaw test. It will be a major and important challenge to develop a fracture mechanics rationale that reconciles these small specimen and nozzle corner flaw test results. These test results are being made available to allow their use by a wide variety of organizations in developing such a rationale, which would be a significant contribution to quantifying the flaw tolerance of reactor pressure vessels.