Heavy metals processing near-net-forming summary progress report

摘要

This study utilized a converging-diverging nozzle to spray-form an alloy having a weight percent composition of 49.6% iron, 49.6% tungsten, and 0.8% carbon into samples for analysis. The alloy was a surrogate that displayed metallurgical characteristics similar to the alloys used in the heavy metals processing industry. US DOE facilities are evaluating advanced technologies which can simplify component fabrication, reduce handling steps, and minimize final machining. The goal of producing net-shaped components can be approached from several directions. In spray forming, molten metal is converted by a nozzle into a plume of fine droplets which quickly cool in flight and solidify against a substrate. The near-final dimension product that is formed receives additional benefits from rapid solidification. This single-step processing approach would aid the heavy metals industry by streamlining fabrication, improving production yields, and minimizing the generation of processing wastes. This Program effort provided a large selection of as-sprayed specimens. These samples were sprayed with gas-to-metal mass ratios ranging from 0.8:1 to 4:1. Samples targeted for analysis were produced from different spray conditions. Metallography on some samples revealed areas that were fully dense and homogeneous at 5,000X. These areas averaged grain sizes of 1 micron diameter. Other samples when viewed at 2,000X were highly segregated in the 10 micron diameter range. Deposit efficiencies of greater than 90% were demonstrated using the untailored spray system. Discharge gases were analyzed and two categories of particles were identified. One category of particle had a chemical composition characteristic of the alloy being sprayed and the second type of particle had a chemical composition characteristic of the ceramics used in the spray system component fabrication. Particles ranged in size from 0.07 to 3 microns in diameter. 8 refs., 67 figs., 20 tabs.