High temperature deformation in 2036 Al and 0.2 wt % Zr-2036 A1

摘要

The microstructure and high-temperature deformation of 2036 Al and a 0.2 wt % Zr modified 2036 Al were characterized. A particle-simulated- nucleation process was applied to refine grain structure in both alloys. Thermomechanically processed materials were tested from 450 to 500 C and strain rates from 2(times)10(sup (minus)1) to 2(times)10(sup (minus)4)s(sup (minus)1). Strain rate sensitivity exponent, activation energy, and total elongation were measured, and the deformation mechanism was proposed. Effect of Zr on microstructure and deformation of 2036 Al at elevated temperatures was discussed.