Preparation of high quality YBa2Cu3O(7-delta) thick films on flexible Ni-based alloy substrates with textured buffer layers

摘要

High current YBa2Cu3O(7-delta) (YBCO) thick films on flexible nickel substrates with textured buffer layers were deposited by using ion beam assisted deposition (IBAD). Pulsed laser deposited YBCO films were not only c-axis oriented with respect to the film surface but also strongly in-plane textured. The in-plane mosaic spread of YBCO films was (approximately) 10(degrees). A critical current density of 8x10(sup 5) A/cm(sup 2) was obtained at 75 K and zero field for thin YBCO films. It was also demonstrated that thick YBCO films with a high critical current and excellent magnetic field dependence at liquid nitrogen temperature can be obtained on flexible nickel substrates by using the textured buffer layers. Issues encountered in producing the films were discussed.