Investigation of the liquid low-level waste evaporator steam coil failure and supporting laboratory studies

摘要

Using a remote video camera, the internals of a low-level waste evaporator tank (termed 2A2, type 304L stainless steel construction, known to have failed steam coils) were inspected. This inspection revealed at least three rather substantial holes as opposed to crack- or pit-like leak sites near the nominal solution level position on one particular steam coil. This section was removed from the evaporator vessel, and subsequent hot cell examination revealed extensive general corrosion on the process side of the coil with little or no attack on the steam side. Hot cell metallography confirmed intense general corrosion on the process side and, in addition, revealed shallow intergranular attack at the leading edge of corrosion. No pits or cracks were detected in this section of the steam coil. Laboratory corrosion tests with coupons of 304L (and other high-alloy materials) isothermally exposed in a range of solutions similar to those expected in the evaporator reveal only very low corrosion rates below 40% sodium hydroxide and the solution boiling point. However, 'dried film' experiments revealed that much more dilute solutions became aggressive to stainless steel due to concentrating effects (evaporation and periodic wetting) at the air/solution interface. The high general corrosion rates observed on the failed coil section occurred at or near the air/solution interface and were attributed to such 'splash zone' activity.