Microstructural dependence of cavitation damage in polycrystalline materials. Final report, 1 November 1992--31 October 1994

摘要

Microstructure of a sample of Inconel X-750 damaged by ISCC (intergranular stress corrosion cracking) was examined after fatigue precracking in a high-temperature environment of deaerated water. Orientation imaging microscopy was used to reveal the microstructure adjacent to the crack path. General high-angle boundaries were found to be most susceptible to cracking. An ordering of the susceptibilities to ISCC damage was proposed; all boundaries have been classified into one of 12 categories. A model is proposed to predict the crack path for ISCC based on ex situ record of damage probabilities. The cracking is modeled as a Markov chain on a regular hexagonal array of grain boundaries representing the connectivity of the network.