Corrosion behaviour of zinc and aluminium in simulated nuclear accident environments

摘要

The corrosion rates of zinc and aluminium were determined in simulated large pipe break and in severe accident cases. An in situ on fine measurement technique, which is based on the resistance measurement of sample wires, was used. In the large pipe break case the corrosion rates of zinc and aluminium were determined at pH 8 and pH 10 in deaerated and in aerated solutions. Tests were also performed in aerated 0.1 M borate buffer solution at pH 9.2. Temperature range was 130 deg C - 50 deg C. The corrosion of zinc appears to be relatively fast in neutral or mildly alkaline aerated water, while both high pH and deaeration tend to reduce the corrosion rates of zinc. The aeration and pH elevation decrease the corrosion rate of aluminium. The simulation of the severe accident case took place in the pH range 3-11 in chloride containing solutions at 50 deg C temperature. The corrosion rate of aluminium was lower than that of zinc, except for the solution with pH 11, in which the corrosion rate of aluminium was practically identical to that of zinc. Both metals corroded more rapidly in the presence of chlorides in acidic and alkalic conditions than in the absence of chlorides at neutral environment. The solubility of zinc and aluminium and the stability of the corrosion products were estimated using thermodynamical calculations. The experimental results and the thermodynamical calculations were in fair agreement. (8 refs.). (Atomindex citation 28:036009)