Tritium and Decay Helium Effects on Cracking Thresholds and Velocities inStainless Steel

机译：氚和朽氦对不锈钢开裂阈值和速度的影响

获取原文

页面导航

摘要
著录项
相似文献
相关主题

摘要

Crack initiation and propagation were studied in three tritium-exposed stainlesssteels. The purpose was to measure cracking thresholds and velocities as a function of helium concentration in Type 21-6-9 stainless steel and 304L steels.

著录项

作者
Morgan, M. J.;
展开▼
作者单位

展开▼
年度 2000
页码 1-8
总页数 8
原文格式 PDF
正文语种 eng
中图分类工业技术;
关键词
Stainless steels; Decay; Helium; Steels; Tritium; Cracks; Crack propagation;

机译：不锈钢;腐烂;氦;钢;氚;裂纹;裂纹扩展;

相似文献

外文文献
中文文献
专利

1. EFFECT OF TRITIUM AND DECAY HELIUM ON THE FRACTURE TOUGHNESS PROPERTIES OF STAINLESS STEEL WELDMENTS [J] . Michael J. Morgan, Scott West, Michael H. Tosten Fusion Science and Technology . 2008,第2期

机译：RIT和衰变氦对不锈钢焊缝断裂韧性的影响
2. Tritium decay helium-3 effects in tungsten [J] . M. Shimada, B.J. Merrill Nuclear Materials and Energy . 2017,第4期

机译：钨中Tri的衰变氦3效应
3. THRESHOLD HELIUM CONCENTRATION REQUIRED TO INITIATE CRACKING DURING WELDING OF IRRADIATED STAINLESS STEEL [J] . Wang CA., Chin BA., Grossbeck ML. Journal of Nuclear Materials: Materials Aspects of Fission and Fusion . 1995,第0期

机译：辐照不锈钢在焊接过程中需要阈值氦气浓度以开始开裂
4. Tritium and decay helium effects on cracking thresholds and velocities in stainess steel [C] . Michael J.Morgan, Michael H.Tosten Topical meeting on the technology of fusion energy . 2000

机译：和衰变氦气对不锈钢开裂阈值和速度的影响
5. Experimental and theoretical characterization of near-threshold fatigue crack growth for high strength steels in seawater [D] . Yang, Jingjun 1995

机译：高强度钢在海水中近阈疲劳裂纹扩展的实验和理论表征
6. The Velocity of Propagation of Brittle Cracks in Steel [O] . M. Greenfield, G. Hudson 1945

机译：钢中脆性裂纹扩展的速度
7. Tritium and Decay Helium Effects on Cracking Thresholds and Velocities in Stainless Steel [O] . Michael J. Morgan, Michael H. Tosten 2001

机译：氚与衰减氦气对不锈钢裂缝阈值和速度的影响

Tritium and Decay Helium Effects on Cracking Thresholds and Velocities inStainless Steel

摘要

著录项

相似文献

相关主题

期刊订阅