Stress Corrosion Crack Growth Rates for Alloy 82H Welds

机译：82H合金焊缝的应力腐蚀裂纹扩展速率

获取原文

页面导航

摘要
著录项
相似文献
相关主题

摘要

Characterize the SCC behavior of 82H welds at temperatures between 288 degrees C and 360 degrees C.

著录项

作者
Mills, W. J.; Brown, C. M.;
展开▼
作者单位

展开▼
年度 2002
页码 p.1-24
总页数 24
原文格式 PDF
正文语种 eng
中图分类工业技术;
关键词
Inconel 82; Stress corrosion; Welded joints; Crack propagation; Microstructure; Fracture properties;

机译：Inconel 82;应力腐蚀;焊接接头;裂纹扩展;显微组织;断裂性能;

相似文献

外文文献
中文文献
专利

1. Microstructural change of the HAZ in an MIG welded bond on an AA7020 aluminium alloy: stress corrosion crack growth rate in dissimilar metal welds [J] . C A BLOEM, M D SALVADOR, V AMIGO Welding International . 2004,第7期

机译：AA7020铝合金上MIG焊缝中的热影响区的组织变化：异种金属焊缝中的应力腐蚀裂纹增长率
2. Stress corrosion cracking initiation and short crack growth behaviour in Alloy 182 weld metal under simulated boiling water reactor hydrogen water chemistry conditions [J] . Bai Juxing, Ritter Stefan, Seifert Hans-Peter, Corrosion science . 2018,第feba期

机译：模拟沸水反应堆氢水化学条件下182合金焊接金属的应力腐蚀开裂和短裂纹扩展行为
3. Slow strain rate stress corrosion cracking behaviour of as-welded and plasma electrolytic oxidation treated AZ31HP magnesium alloy autogenous laser beam weldment [J] . P. Bala Srinivasan, S. Riekehr, C. Blawert, Materials Science and Engineering . 2009,第1a2期

机译：AZ31HP镁合金自生激光束焊接及等离子电解氧化处理后的慢应变速率应力腐蚀开裂行为
4. DEVELOPMENT OF CRACK GROWTH RATE DISPOSITION CURVES FOR PRIMARY WATER STRESS CORROSION CRACKING (PWSCC) OF ALLOY 82,182, AND 132 WELDMENTS [C] . G. A. White, N. S. Nordmann, J. Hickling, 12th International Conference on Environmental Degradation of Materials in Nuclear Power Systems: Water Reactors 2005 vol.2 . 2005

机译：合金82,182和132焊件的主要水应力腐蚀开裂（PWSCC）的裂纹增长率分布曲线的开发
5. Indications of Stress Corrosion Cracking Resistance in Alloy 82 Dissimilar Metal Welds in Simulated Primary Water Environments [D] . Persaud, Suraj 2011

机译：模拟的一次水环境中82合金异种金属焊缝的耐应力腐蚀开裂迹象
6. Stress Corrosion Cracking of Friction Stir-Welded AA-2024 T3 Alloy [O] . Marina Cabrini, Sara Bocchi, Gianluca D’Urso, 2020

机译：搅拌摩擦焊接AA-2024 T3合金的应力腐蚀开裂
7. EFFECT OF UNBROKEN LIGAMENTS ON STRESS CORROSION CRACKING BEHAVIOR OF ALLOY 82H WELDS [O] . Mills, W.J. and Brown, C.M. 2003

机译：UNBROKEN LIGamENTs对合金82H焊缝应力腐蚀开裂行为的影响

Stress Corrosion Crack Growth Rates for Alloy 82H Welds

摘要

著录项

相似文献

相关主题

期刊订阅