Glass Selection Strategy: Development of US and KRI Test Matrices

摘要

High-level radioactive wastes are stored as liquids in underground storage tanks at the Department of Energys (DOE) Savannah River Site (SRS) and Hanford Reservation. These wastes are to be prepared for permanent disposition in a geologic repository by vitrification with glass forming additives (e.g., frit), creating a waste form with long-term durability. Wastes at SRS are being vitrified in the Defense Waste Processing Facility (DWPF). Vitrification of the wastes stored at Hanford is planned for the Waste Treatment and Immobilization Plant (WTP) when completed. Some of the wastes at SRS, and particularly those at Hanford, contain high concentrations of aluminum, chromium and sulfate. These elements make it more difficult to produce a waste glass with a high waste loading (WL) without crystallization occurring in the glass (either within the melter or upon cooling of the glass), potentially exceeding the solubility limit of critical components, having negative impacts on durability, and/or resulting in the formation of a sulfate salt layer on the molten glass surface. Although the overall scope of the task is focused on all three critical, chemical components, the current work will primarily address the potential for crystallization (e.g., nepheline and/or spinel) in high level waste (HLW) glasses. Recent work at the Savannah River National Laboratory (SRNL) and by other groups has shown that nepheline (NaAlSiO4), which is likely to crystallize in high-alumina glasses, has a detrimental effect on the durability of the glass.