Review of Experimental Methods for Determining Residual Creep Life

摘要

Experimental methods available for determining how much creep life remains at a particular time in the high temperature service of a component are reviewed. After a brief consideration of the limitations of stress rupture extrapolation techniques, the application of post-exposure creep testing is considered. Ways of assessing the effect of microstructural degradation on residual life are then reviewed. It is pointed out that while this type of work will be useful for certain materials, there are other materials in which 'mechanical damage' such as cavitation will be more important. Cavitation measurement techniques are therefore reviewed. The report ends with a brief consideration of the use of crack growth measurements in assessing the residual life of cracked components. (Atomindex citation 09:385868)