Hot-Dipped Tin-Zinc on U-0.75 W/O Ti

摘要

Conventional Zn galvanizing of U-0.75 Ti results in nonuniform coatings and reduced elongation because of thermal aging of the surface of the U-Ti. A lower melting material which would give sacrificial galvanic protection to the U-Ti was found in the Sn-Zn alloy system. The present work describes: (1) the metallography of the Sn-Zn system, (2) the electrochemistry of the Sn-Zn system with respect to U-Ti, (3) the mechanics of applying a Sn-Zn coating to U-Ti, (4) salt spray corrosion test results of various Sn-Zn alloys applied to U-Ti coupons, and (5) mechanical property tests of coated U-Ti tensile bars. An 80 Sn-20 Zn alloy (MP-280 exp 0 C) was chosen for the galvanizing study because of its lower melting point. The results showed that all alloys of the Sn-Zn system galvanically protected the U-Ti in salt fog environments. The lack of a suitable low temperature flux prevented the operation of the Sn-Zn bath at its optimum temperature and low elongations were obtained with this coating system. (ERA citation 04:056877)