Electrical Resistivity and Dechanneling Study of Radiation Defects in Iron by exp 235 U Fission Fragments (F.F.). I - Study of Damage Induced by F.F. Irradiation at 20K. II - Recovery of Radiation Defects

摘要

The irradiation by exp 235 U fission fragments (F.F.) of two iron samples of different purities (the essential impurity being C) have been studied. Comparative measurements of electrical resistivity and dechanneling of 5 MeV alpha -particles have been made during irradiation and subsequent recovery. The production curves provide, from their slopes at the origin, the following informations: 14000 Frenkel pairs by F.F. (from electrical resistivity); aggregate's rate: 5 per mille (from dechanneling). These curves do not follow a simple law: it seems that one observes the superposition of two saturation mechanisms with very different kinetics. During recovery, the same stages that after electrons or neutrons irradiation are observed, but with very different proportions. Dechanneling puts in evidence: -great modifications in cementite precipitation of an Fe-C alloy, by irradiation; - the recovery stage of loops starting from 800 K and with an activation energy approximately 1 eV; - the preponderant effect of clustering during stages Isub(D), Isub(E), IIsub(C) and IIsub. (Atomindex citation 11:524938)