Magnetic Susceptibility of Scandium-Hydrogen and Lutetium-Hydrogen Solid-Solution Alloys from 2 to 300 exp 0 K

摘要

Results for pure Sc show that the maximum and minimum in the susceptibility discovered earlier are enhanced as the impurity level of iron in scandium decreases. The Stoner enhancement factor, calculated from low-temperature heat capacity data, susceptibility data, and band-structure calculations show Sc to be a strongly enhanced paramagnet. Below 2 exp 0 K, the magnetic anisotropy between the hard and easy directions of scandium decreases linearly with decreasing temperature, tending toward zero at 0 K. The large increase in the susceptibility of Sc at lower temperatures indicates magnetic ordering. Pure Lu and Lu-H alloys showed an anisotropy in susceptibility vs orientation; thus the samples were not random polycrystalline samples. Pure Lu shows the shallow maximum and minimum, but the increase in susceptibility at low temperatures is larger than previously observed. The susceptibility-composition dependence of the Lu-H alloys also did not match other data. The susceptibility-composition dependence does not match the composition dependence of the electronic specific heat constant below 150 K, showing the electronic specific heat is being affected by terms other than phonon-electron and pure electron-electron interactions. (ERA citation 08:012681)